HOW HOW TO MEASURE THE ENERGY USED TO FIRE CLAY BRICKS
PRACTICAL FIELDA PRACTICAL GUIDE FOR BRICKMAKERS, FIELD-WORKERS AND RESEARCHERS Introduction
In 1996 ITDG (now known as Practical Action) undertook a project working with small-scale brickmakers in Peru, Ecuador and Zimbabwe. The idea is to disseminate appropriate, energy efficient principles and practices. But what is an energy efficient brick firing technology? How do you measure it? And how do you compare it with technologies used in other places? Data on energy use in brickmaking has generally been collected and presented in a random fashion. It's often of very little use when trying to evaluate and compare processes. For example, a report may state 'brickmakers use four sacks of coal to fire a thousand bricks.' Fine, but what does this tell us about the energy used? We don't know the mass of a sack of coal. We don't know its calorific value. And we don't know anything about the bricks. What type of soil are they made from, and how much heat is needed for vitrification - the formation of the ceramic bond? How wet were they going to the kiln - how much fuel was used simply to dry them? What is their mass? (Bigger, heavier bricks obviously take more energy to fire.) And how well burned are they? In short, we know next to nothing useful. This technical brief details a way of gathering and presenting information on brick firing. If the method is followed, it will allow not only the energy use of a particular kiln to be calculated, but also the efficiency to be compared to others world-wide. There are difficulties involved in Figure 1: Brickmaker lighting a kiln establishing a with a liquid fuel burner. Photo: methodology. For Practical Action. example, some scientific knowledge is implicit. Also, facilities around the world and the resources available to those monitoring brick firing will be different. As far as possible, the method presented here minimises costs and the need for specialist services.
Figure 2: Firing bricks using wood as a fuel. Photo:
Practical Action.
Practical Action, The Schumacher Centre, Bourton on Dunsmore, Rugby, Warwickshire, CV23 9QZ, UK T +44 (0)1926 634400 | F +44 (0)1926 634401 | E infoserv@practicalaction.org.uk | W www.practicalaction.org ______________________________________________________________________________________________ Practical Action is a registered charity and company limited by guarantee. Company Reg. No. 871954, England | Reg. Charity No.247257 | VAT No. 880 9924 76 | Patron HRH The Prince of Wales, KG, KT, GCB
How to measure the energy used to fire clay bricks
Practical Action
Background Background
The factors which affect energy use in brickmaking are: • The nature of the clay: refractoriness - resistance to change by heat; the presence of fluxes - substances which aid vitrification; intrinsic calorific value. • The moisture content of 'green' bricks going into the kiln. • The type of fuel used, its calorific value, moisture content, and distribution. • The design of kiln. • The skill of the brickmakers controlling the burning process • The climatic conditions: ambient temperature, wind direction and strength... Normally, it's the effect of kiln design which is being investigated. Either that or varying the operating conditions of similar kilns. Here, the way we gather data takes account of the nature of the clay and its effect on energy consumption. We also consider only the energy used in firing, ruling out drying energy, so we can compare processes directly. Then we propose a way of measuring how much heat-work has actually been done - this is so we can take account of how well bricks are fired. (It would be easy to think a process was efficient because it used very little energy and then find the bricks were only dried mud - not vitrified at all!)
Data Data collection
We categorise clay as high temperature (vitrifying above 1,000°C), medium temperature (vitrifying between 950 and 1,000°C), or low temperature (vitrifying below 950°C). This means access to a laboratory kiln which can reach such temperatures. The procedure is to mould cones approximately 70 mm high with a base diameter around 15 mm. Cones are placed in the kiln leaning slightly so that when vitrification temperature is reached the top bends over. This temperature is noted and the clay categorised accordingly. The exact number of bricks being fired is needed. This is easier to determine if bricks are stacked in thousands prior to firing. Alternatively, the bricks in each layer can be counted as the kiln is built. Then we need to know the mass of the bricks. A convenient number of green bricks (perhaps 1 per 1,000, but not less than 24) should be selected at random and weighed. Thence an average 'wet mass' can be calculated. Now we need to know the moisture content of the green bricks to calculate the energy needed simply to dry them. The selected bricks can be dried in a conventional oven or a simple field oven. The important thing is to keep bricks between 80 and 100°C and weigh them periodically until no further weight loss is noted. The average 'dry mass' can then be found. With this data it's possible to calculate the mass of water and the drying energy: Moisture content = wet mass - dry mass wet mass
(wet basis)
Mass of green bricks = Total moisture content Drying energy =
avg. mass of green brick x no. of bricks = moisture content of brick x mass of bricks
specific drying energy x total moisture content
(Where specific drying energy' = 2,591 kJ/kg of moisture)
All fuel used should be weighed. If a fuel such as sawdust or pulverised fly ash is mixed into the body of bricks, its mass must also be determined. A sample of each fuel used should be taken promptly to test for calorific value and moisture content. If the clay has a natural fuel content, it too should be sent for testing. If such test facilities are unavailable or unaffordable, then the best that can be done is to use the most recent local data. If a value is found in this way, it should not be recorded as the
2
How to measure the energy used to fire clay bricks
Practical Action
specific calorific value and a note should be made of the source of the information. From this data the total energy used is calculated: Total energy = mass of fuel x net calorific value
And the firing energy is obtained by subtracting the energy used for drying Firing energy = total energy - drying energy
We need to know how well bricks are fired, or rather the heat-work done. Testing brick properties such as compressive strength will not give useful data to compare kilns because properties are affected by factors other than firing. The effectiveness of a firing process is a function of time and temperature, but the relationship is not linear. Bricks fired at 1,000°C for 10 hours would not be the same as bricks fired at 100°C for 100 hours! We could plot temperature against time for various points in the kiln and present this graphically to qualify energy use. However, thermometry to measure such high temperatures is expensive1. A more affordable alternative is to use Buller's Bars2 placed strategically in the kiln. Buller's Bars are about 57 mm long and are made from ceramic material which melts at set temperatures. They come in a range from 590 to 1,525°C. Four bars which melt at different temperatures can be placed on a refractory stand to form a 'thermoscope'. Thermoscopes are placed as required in the kiln. Once the kiln is fired and cooled, a representative sample of bricks - the same number as before - should be weighed, and the average fired mass calculated. Now we can calculate the total mass of fired brick and the specific firing energy: Mass of fired brick = mass of a fired brick x number of fired bricks Firing energy Mass of fired brick
Specific firing energy =
Presenting Presenting results
Ultimately, the results of a brick firing process would consist of: • • • • The specific energy used. The moulding process. The clay vitrification temperature categorisation. The Buller's Bar numbers for different locations, and/or an average number. A statement of qualifying information, comments and observations
•
This brief contains a photocopiable monitoring form for recording data and calculations. There is also an example of a completed form for guidance, and a checklist to ensure all the vital data has been recorded. .
1
At 1998 prices, thermometry to monitor a 20,000 brick kiln would cost approximately £1,500 (obviously this hardware should be re-usable). Using Buller's Bars would cost about £70 per kiln. 2 Buller's Bars can be obtained from Taylor Tunnicliff Ltd., Normacot Road, Longton, Stokeon-Trent, ST3 1PA, UK; tel. 44 (0)1782 501174; fax. 44 (0)1782 328807.
3
How to measure the energy used to fire clay bricks
Practical Action
Checklist Checklist
The following is a list of information which must be noted: (1) Name of brickmaker, location and/or address of brickworks
(2)
Clay type in terms of its vitrification temperature Moulding process Type of kiln Start and finish dates and times (duration of firing) Weather conditions Exact number of green bricks going into the kiln Mass of green bricks Mass of dry bricks Mass of fuel(s) used in the kiln Calorific value of the fuel(s) Heat-work done (Buller's Bar numbers) Mass of fired bricks
(3)
(4)
(5)
(6)
(7)
(8)
(9)
(10)
(11)
(12)
(13)
4
How to measure the energy used to fire clay bricks
Practical Action
MONITORING MO MONITORING FORM: Energy consumption of brick firing processes
Name Name of producer Fambidzanai Training Centre (FTC) Type of Type of clamp/kiln Layered, scoved clamp Calorific Calorific value (kJ/kg) Gross 20,170 19,180 Net Moisture content (%) ? Brick moisture content (%) Brick = (3.65 - 3.25) x 100/3.65 = 10.96 (wet basis) Location/address 4 Dovedale Rd, Stapleford, Mount Hampden, Harare. Type of fuel Boiler waste No. of green bricks in kiln 14,817 Dates and times of firing Start 1 Jan. 1998 Finish 15 Jan. 1998 Mass of fuel used (kg) 4,680 Mass per brick (kg) 3.65 green 3.25 dry 3.10 fired Weather conditions Intermittent heavy rain, but clamp sheltered by roof Qualifying information: (i) Soil vitrification category High temperature (>1000°C) Bar (ii) Bullers Bar no. = 13 (≈ 890°C)‡ And/or (iii) (iii) Avg. firing temp. (°C) ? (iv) Firing time (hrs) ?
Method of forming Semi-dry pressing press machine)
(Ceratec
Calculation efficiency Calculation of kiln efficiency Mass of green brick (kg) 14,817 x 3.65 = 54,082 Mass of dry brick (kg) 14,817 x 3.25 = 48,155 Total moisture content (kg) 14,817 x (3.65 - 3.25) = 5,927 Drying energy (kJ) 2,591 x 5,987 = 15,356,857 Total energy (kJ) 4,680 x 19,180 = 89,762,400 Firing energy (kJ) 89,762,400 - 15,356,857 = 74,405,543 Mass of fired brick (kg) 3.10 x 14,817 = 45,933 Specific firing energy (kJ/kg) 74,405,543/45,933 =1,620
Notes: Notes Notes ‡Thermoscopes contained bars 11, 13, 15 & 17. Only six of eighteen were recovered. Three from the sides of layers 4 and 15 and the centre of layer 26 were virtually unaffected. One from the side of layer 8 showed Bar no. 13 just sagging. Two, from layer 14 (centre) and layer 18 (side) had all the bars melted - turned totally to liquid in layer 14. With only six samples it's not really valid to take an average. Comments: Bricks are mostly underfired. Specific firing energy is thus quite low. The long firing time indicates not enough air gaps - boiler waste packs 'tighter' than coal. Brick quality and appearance is not good due to poor soil preparation, a worn press machine, and contamination from to drying on dirty ground. Bricks are easily broken, revealing no unfired core, but a matrix containing lumps of dry clay and stones - stones too big to make a strong brick. Bricks aren't vitrified but merely quite well 'baked'. Some were 'hard-burned' - turning blue. These corresponded to 'hot-spots' indicated by Thermoscopes. Clamp volume is 39 cubic metres while the volume of bricks is around 27 cubic metres. Void volume is thus 12 cubic metres (about 30%) which includes the volume of coal initially in the clamp. Recommendations: Green bricks should be thoroughly dry to save fuel. The firing process needs modifying to produce well-burned bricks. The 'high temperature' soil is difficult to vitrify, needing a temperature of more than 1000°C. Experience suggests fuel should be increased by around 20%. More sensibly, this increase could be achieved by ensuring green bricks are dry. The same fuel to brick mass ratio could then be retried. The other problem is air flow. The clamp burned too slowly. Boiler waste could be distributed more evenly throughout, and air gaps between bricks could be increased. Firing time could be reduced to around 7 days. date, Signature, date, organisation & contact address Kelvin Mason, IT-Zimbabwe, PO Box 1744, Harare. Tel: 490270, 496653, 496746/7 Fax: 496041
5